(mouse over)
![]() |
| Property | Li-98 | Li-98C | Li-98CN | Li-98P | Unit | Test Method | ||
Thickness |
0.15 |
0.25 |
0.2 |
0.18 |
0.1 |
0.14 |
- |
ASTM D374 |
Color |
White |
White |
White |
White |
White |
White |
- |
Visual |
Reinforcement Carrier |
fiberglass mesh |
- |
polymide |
- |
- |
|||
Density |
1.85 |
1.85 |
1.9 |
1.8 |
1.3 |
1.2 |
g/cm3 |
ASTM D792 |
Tensile Strength |
200 |
400 |
200 |
50 |
500 |
600 |
psi |
ASTM D412 |
Glass Transition Temperature |
-30 |
-30 |
-27 |
-30 |
-25 |
-25 |
℃ |
- |
Short time Use Temperature(30 sec) |
200 |
200 |
200 |
200 |
250 |
250 |
℃ |
- |
Continuous Working Temperature |
-30 ~ 120 |
-30 ~ 120 |
-30 ~ 120 |
-30 ~ 120 |
-30 ~ 120 |
-30 ~ 120 |
℃ |
- |
Thermal Conductivity |
0.95 |
0.95 |
1.8 |
2 |
1.7 |
1.7 |
W/mK |
ASTM D5470 |
Thermal Impedance @ <1psi |
1.0 |
1.8 |
0.7 |
0.6 |
0.8 |
0.9 |
℃in2/W |
ASTM D5470 |
Thermal Impedance @ 50psi |
0.9 |
1.5 |
0.5 |
0.3 |
0.6 |
0.7 |
℃in2/W |
ASTM D5470 |
Initial Tack |
11 |
10 |
14 |
15 |
15 |
15 |
cm |
PSTC-6 |
Lap Shear Strength. |
61 |
61 |
65 |
55 |
63 |
62 |
N/cm2 |
ASTM D1002 |
Die Shear Strength@25℃ |
120 |
120 |
118 |
100 |
115 |
115 |
N/cm2 |
- |
Die Shear Strength@80℃ |
69 |
69 |
68 |
55 |
66 |
64 |
N/cm2 |
- |
Holding Power 1000g@25℃using 1 in2 |
>10000 |
>10000 |
>10000 |
>10000 |
>10000 |
>10000 |
min |
PSTC-7 |
Holding Power 1000g@80℃ using 1 in2 |
>10000 |
>10000 |
>10000 |
>10000 |
>10000 |
>10000 |
min |
PSTC-7 |
90∘Peeling Strength (aluminum) |
>10 |
>12 |
>10 |
>10 |
>10 |
>10 |
N/in |
ASTM D3330 |
Dielectric Breakdown Voltage (Vac) |
2000 |
3000 |
3000 |
3000 |
4000 |
5000 |
V |
ASTM D149 |
Dielectric Breakdown Voltage (Vdc) |
3000 |
4000 |
4000 |
4000 |
5000 |
6000 |
V |
ASTM D149 |
|
||||||||